1. Recrystallization Kinetics of Fe-3%Si after Deformation at High Strain Rate and High Temperature
Recrystallization kinetics of Fe-3%Si with initial grain size 296~839µm at the temperature range 1223~1423K, strain range from 0.51 to 0.92, strain rate range 5~80s−1 was studied by isothermal compression test using Gleeble-2000. The effect of strain, strain rate, initial grain size and annealing temperature on the recrystallization kinetics were discusse
Mat. Res.. Publicado em: 07/11/2019
-
2. Avaliação da susceptibilidade à corrosão de um aço inoxidável AISI 316L submetido à simulação térmica com o uso da Gleeble
RESUMO Este trabalho teve como finalidade avaliar a influência do tamanho médio dos grãos na susceptibilidade à corrosão do aço inoxidável austenítico AISI 316L, cujo material é bastante utilizado em juntas soldadas, em temperatura ambiente e em baixíssimas temperaturas (condições criogênicas) por apresentar excelente resistência à corrosão e
Matéria (Rio J.). Publicado em: 16/09/2019
-
3. Effect Of The Application Of Constant And Variable Temperatures at the Overaging Stage in the Mechanical Properties of Trip780 Steel
The effect of the application of constant temperatures (isothermal plateau) and variables (cooling ramp) during the overaging (OA) stage of the continuous annealing cycle in the microstructural characteristics and mechanical properties of a TRIP steel of the class of 780 MPa was investigated. It was simulated six overaging conditions in the equipment Gleeble
Mat. Res.. Publicado em: 15/07/2019
-
4. Effect of Processing Parameters on Hot Deformation Behaviour and Microstructural Evolution of PM Ti-5553 Alloy at a Moderate-high Strain Rate
Isothermal compression tests of Ti-5553 (Ti-5Al-5V-5Mo-3Cr) alloy, produced by a fast consolidation approach from blended elemental powder mixture, were performed on a Gleeble® 3800 thermal-physical simulator to investigate its hot deformation behaviour. The samples were compressed in a wide temperature range from 700 ºC to 1150 ºC and a moderate-high str
Mat. Res.. Publicado em: 10/06/2019
-
5. Influência do Ciclo Térmico de Soldagem no Crescimento de Grão, nas Transformações Microestruturais e na Formação de MA na GGZAC de aço TMCP
Resumo A soldagem com elevado aporte térmico é uma das alternativas adotadas pelos estaleiros e fabricantes de torres eólicas para aumento da produtividade. No entanto, os ciclos térmicos gerados no processo podem provocar transformações microestruturais prejudiciais à tenacidade na zona afetada pelo calor, especialmente na região de grãos grosseiro
Soldag. insp.. Publicado em: 09/05/2019
-
6. Avaliação da Aplicação de um Atlas de Soldagem de um Aço Bainítico Microligado ao Nióbio
Resumo Os aços de alta resistência microligados ao nióbio têm mostrado ser uma boa opção para fabricação de perfis estruturais, utilizando os conceitos já desenvolvidos para a indústria de gás e óleo. Entretanto, a definição das reais necessidades em termos de soldagem desta família de aços não está bem descrita nas normas de soldagem mais
Soldag. insp.. Publicado em: 2017-06
-
7. Numerical Description of Hot Flow Behaviors at Ti-6Al-2Zr-1Mo-1V Alloy By GA-SVR and Relative Applications
Hot compression tests of as-cast Ti-6Al-2Zr-1Mo-1V alloy in a wide temperature range of 1073-1323 K and strain rate range of 0.01-10 s-1 were conducted by a servo-hydraulic and computer-controlled Gleeble-1500 machine. The hot flow behaviors of Ti-6Al-2Zr-1Mo-1V alloy show highly non-linear relationships with strain, strain rate and temperature. In order to
Mat. Res.. Publicado em: 29/09/2016
-
8. Modelling the Hot Flow Behaviors of AZ80 Alloy by BP-ANN and the Applications in Accuracy Improvement of Computations
Hot compressions of as-cast AZ80 magnesium alloy in a wide temperature range of 523-673 K and strain rate range of 0.01-10 s–1 with a height reduction of 60% were conducted by a Gleeble-1500 thermo-mechanical test simulator. The hot flow behaviors show highly non-linear intrinsic relationships with temperature, strain and strain rate. In order to model the
Mat. Res.. Publicado em: 03/11/2015
-
9. The flow behavior modeling of as-extruded 3Cr20Ni10W2 austenitic heat-resistant alloy at elevated temperatures considering the effect of strain
In order to investigate the compressive deformation behavior of 3Cr20Ni10W2 alloy, a series of isothermal upsetting experiments were carried out in the temperature range of 1203-1403 K and strain rate range of 0.01-10 s-1 on a Gleeble-1500 thermo-mechanical simulator. The results indicate that the flow stress initially increases to a peak value and then decr
Mat. Res.. Publicado em: 18/02/2014
-
10. Avaliação do impacto do titânio e carbono equivalente na ductilidade a quente dos aços médio carbono
O objetivo desse trabalho é avaliar o impacto do titânio e carbono na ductilidade a quente de aços médio carbono com e sem a presença de titânio. Para isto, foi utilizado o simulador termomecânico Gleeble® 3500, na realização dos ensaios de ductilidade a quente e o Microscópio Eletrônico de Varredura (MEV), para análise do aspecto da fratura. Pa
Rem: Rev. Esc. Minas. Publicado em: 2013-12
-
11. Effect of temperatures and strain rates on the average size of grains refined by dynamic recrystallization for as-extruded 42CrMo steel
In order to study the dynamic recrystallization (DRX) behavior of as-extruded 42CrMo high-strength steel, a series of isothermal upsetting experiments were carried out in a temperature range of 1123~1348 K and a strain rate range of 0.01~10 s-1 on Gleeble 1500. It was found that DRX softening is more recognizable at higher temperatures and lower strain rates
Mat. Res.. Publicado em: 18/06/2013
-
12. The improved arrhenius model with variable parameters of flow behavior characterizing for the as-cast AZ80 magnesium alloy
In order to study the hot working behaviour of as-cast AZ80 magnesium alloy, a series of isothermal upsetting tests with height reduction of 60% were performed at the temperature range of 523-673 K and the strain rate range of 0.01-10 s-1 on a servo-hydraulic Gleeble-1500 machine simulator. Based on the regression analysis for Arrhenius type equation of flow
Mat. Res.. Publicado em: 14/05/2013