Estudo do comportamento termomecânico do aço API 5L X80 microligado ao Nb-Ti através de ensaios de torção a quente
AUTOR(ES)
Martins, Fernanda Huebra, Machado, Marcelo Lucas Pereira
FONTE
Rem: Rev. Esc. Minas
DATA DE PUBLICAÇÃO
2015-06
RESUMO
AbstractThe controlled rolling of high strength low alloy steel has been widely used in the production of large diameter pipes for the oil and gas industry. The thermo-mechanical control process (TMCP) is used to maximize grain refinement and achieve both higher strength and toughness in the steels. In this sense, API 5L X80 micro-alloyed Nb-Ti steel was submitted to hot torsion tests to evaluate its hot deformation behavior. The critical temperatures (Tnr, Ar3 and Ar1) were obtained by testing with multiple strains in continuous cooling. From the flow stress curves generated in the isothermal tests, it was possible to obtain a critical strain that starts dynamic recrystallization, the peak strain for temperatures ranging from 1150ºC to 850ºC, and the strain rates at 0.2; 0.4 and 0.8s-1. The results showed that peak and critical stress values increase as the temperature decreases and strain rate increases.
Documentos Relacionados
- Obtenção de ferrita de grão utrafino em aços C - Mn e microligado com Nb-Ti através de ensaios de torção a quente
- Estudo do comportamento do aço API 5L X80 quando submetido à soldagem por processo automatizado
- Estudo das tensões residuais de juntas soldadas de aço API 5L X80
- CURVAMENTO POR INDUÇÃO DE TUBO DA CLASSE API 5L X80
- A Comparative Investigation of the Corrosion Resistance and HIC Suceptibility of API 5L X65 and API 5L X80 Steels