Api 5l X80 Steel
Mostrando 1-12 de 20 artigos, teses e dissertações.
-
1. Avaliação Microestrutural e Resistência à Corrosão de uma Junta Dissimilar entre um Aço de Alta Resistência e Baixa Liga e Aço um Inoxidável Duplex
Resumo A união entre materiais dissimilares tem sido amplamente aplicada na indústria de petróleo e gás. Em geral, este tipo de soldagem é mais sensível às diferenças de composição química existente entre os metais envolvidos. Diante dessa perspectiva, este trabalho tem por objetivo avaliar, por união autógena, a microestrutura de uma junta sold
Soldag. insp.. Publicado em: 16/05/2019
-
2. A Comparative Investigation of the Corrosion Resistance and HIC Suceptibility of API 5L X65 and API 5L X80 Steels
High strength low alloy (HSLA) steels are used for the construction of pipelines for oil and natural gas transportation. For such applications pipelines must exhibit mechanical resistance and resistance to corrosion and hydrogen induced cracking (HIC). API 5L X65 steels are the main materials used for this purpose. However, for economic reasons, the use of s
Mat. Res.. Publicado em: 07/01/2019
-
3. Modeling of the temperature field generated by the deposition of weld bead on a steel butt joint by FEM techniques and thermographic images.
The aim of this work is to predict the temperature field generated by welding a steel butt joint (API 5L X80). The prediction was modeled by finite element software Abaqus where the subroutine was developed in Fortran so that heat source motion may be included. The motion was based on the Goldak's double ellipsoid. In the model material nonlinearities were i
Mat. Res.. Publicado em: 23/02/2018
-
4. Corrosion Behavior of API 5L X80 Steel in the Produced Water of Onshore Oil Recovery Facilities
High-strength low-alloy steel is used in pipelines, which transport oil/gas and also produced water in the process of the secondary recovery of oil. This paper investigates the corrosion of X80 steel after immersion in static systems (biotic and abiotic). The corrosion rate, the corrosion morphology and the hardness of the coupons were investigated. The corr
Mat. Res.. Publicado em: 09/10/2017
-
5. Evaluation of Co-Ni/SiC Nanocomposite Coating Obtained by Electrodeposition on the Corrosion Resistance of API 5L X80 Steel
Co-Ni/SiC nanocomposite coatings were obtained by codeposition of SiC nanoparticles in a bath with nickel and cobalt, using API 5L X80 as the substrate. The influence of cathodic current density on deposit properties was investigated. Measurements of electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization (PP) were performed in 3.5 wt%
Mat. Res.. Publicado em: 29/06/2017
-
6. Estudo do comportamento termomecânico do aço API 5L X80 microligado ao Nb-Ti através de ensaios de torção a quente
AbstractThe controlled rolling of high strength low alloy steel has been widely used in the production of large diameter pipes for the oil and gas industry. The thermo-mechanical control process (TMCP) is used to maximize grain refinement and achieve both higher strength and toughness in the steels. In this sense, API 5L X80 micro-alloyed Nb-Ti steel was sub
Rem: Rev. Esc. Minas. Publicado em: 2015-06
-
7. Corrosion Evaluation of SAW Welded API 5L X-80 Joints in H2S-Containing Solution
The H2S corrosion resistance of API 5L X80 steel and its welded joint (WJ) were evaluated using the weight loss method in a 5%wt brine solution and different corrosive environments based on a sodium thiosulphate solution (10–3 and 10–2 mol/l). The weight loss method, scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD) were applied to
Mat. Res.. Publicado em: 2015-04
-
8. Evenmatched FCAW process in API 5L X80 steel welded joint
The evenmatched welding conditions in FCAW-G process were used in API 5L X80 steel. In this study, two joint geometries (bevel 25° and 35°) with different process parameters were used. Each type of joint was welded with one type of consumable: AWS E81T1-Ni1C (evenmatched), with variation of heat input. During welding the voltage and current varied in a ran
Mat. Res.. Publicado em: 24/01/2014
-
9. Analysis of the corrosion scales formed on API 5L X70 and X80 steel pipe in the presence of CO2
Longitudinal welded joints samples of X70 and X80 API grade steel pipes were exposed to a deaerated 1% NaCl solution containing CO2, at temperatures in the range of 25 ºC to 80 ºC for 48 hours. Analogous samples were exposed to the adjacent vapour phase. The layer of corrosion products which formed on the base metal and welded regions of the samples was in
Mat. Res.. Publicado em: 08/11/2013
-
10. Study of phase transformations In API 5L X80 Steel in order to increase its fracture toughness
Phase transformations in API 5L X80 steel were studied in different thermomechanical sequences with a view to increasing the fracture toughness of this steel. Dilatometry tests performed on the quenched steel detected a phase transformation occurred, during heating, in the temperature range 593-618 K. This phase transformation was identified as the dissoluti
Mat. Res.. Publicado em: 19/02/2013
-
11. Análise crítica do ensaio de determinação da curva mestre (ASTM E 1921) aplicado a um aço da classe API 5L X80. / Critique analyse of essay of determination of master curve (ASTM E 1921) applied the an API 5L X80 steel.
One of the key aspects of structural integrity is the consideration of scale effects characteristic of materials wich present quase-brittle behavior. The Master curve method, designed for ferritic steels operating at temperatures in the materials corresponding to the ductile-brittle transition. This method combine charpy impact testing and a few fracture tou
Publicado em: 2011
-
12. Estudo da soldabilidade do tubo API 5L X80 utilizando os processos de soldagem: MAG com transferência controlada e eletrodo tubular. / Study of the weldability of API 5L X80 pipe using the gmaw-stt and fcaw welding process.
Os tubos API 5L X80, construídos com aços alta resistência e baixa liga, são especificados para a construção de dutos para transporte de petróleo e derivados sob alta pressão, com conseqüente redução no peso dos tubos. O processo mais empregado para a soldagem circunferencial de tubos em campo no Brasil é o processo com eletrodo revestido, tanto
Publicado em: 2010