Silorane- and high filled-based"low-shrinkage" resin composites: shrinkage, flexural strength and modulus

This study compared the volumetric shrinkage (VS), flexural strength (FS) and flexural modulus (FM) properties of the low-shrinkage resin composite Aelite LS (Bisco) to those of Filtek LS (3M ESPE) and two regular dimethacrylate-based resin composites, the microfilled Heliomolar (Ivoclar Vivadent) and the microhybrid Aelite Universal (Bisco). The composites (n = 5) were placed on the Teflon pedestal of a video-imaging device, and VS was recorded every minute for 5 min after 40 s of light exposure. For the FS and FM tests, resin discs (0.6 mm in thickness and 6.0 mm in diameter) were obtained (...