LZS/Al2O3 Glass-Ceramic Composites Sintered by Fast Firing

In this work, nanometric Al2O3 (1-5 vol.%) particles (13 nm, 100 m2/g) were added to a 19.58Li2O•11.10ZrO2•69.32SiO2 (mol%) (3.5 µm, 2.5 m2/g) parent glass-ceramic matrix to prepare composites with the purpose of studying the influence of Al2O3 on their structure, microstructure, mechanical, thermal and electrical properties when sintered by fast firing. The parent glass-ceramic was prepared by melting and fast cooling (in water) to obtain a glass frit. The resulting glass frit was milled according to a two-step procedure consisting on a dry milling stage followed by a long wet milling st...