Evaluation of inorganic and organic bone components after application of an apatite-coated Al2O3 implants as scaffolds for bone repair

The aim of this work was to study the influence of uncoated and apatite-coated Al2O3 implants on bone regeneration after 30 days of surgery in New Zealand white rabbits. Twelve samples of Al2O3 implants were prepared and half of them (n = 6) were apatite-coated by the modified biomimetic method. Three experimental groups were tested as Group C - control, surgery procedure without cerami c implant, Group Ce - uncoated Al 2O3 implants (n = 6) and Group CeHA - apatite-coated Al2O3 implants (n = 6). The mineralization of the Al2O3 implants was analyzed in bone fragments using FT-Raman spectroscopy...