1. Bioactive SiO2-K2O-CaO-P2O5 glass-ceramic scaffold prepared using polyurethane foam template
Abstract A glass-ceramic in the SiO2-K2O-CaO-P2O5 quaternary system was prepared by substituting the Na2O component with K2O to avoid Na2Ca2Si3O9 formation upon thermal treatment since this phase decreases apatite formation kinetics on glass material. To form the glass-ceramic, a modified sol-gel method involving solution precipitation, followed by reagents
Cerâmica. Publicado em: 2023
-
2. The influence of compositional variability of dimension stone residues on the properties of rustic porous ceramic tiles
Abstract This study analyzed how the compositional variability of dimension stone residues influences the characteristics of rustic porous ceramic tiles. The specimens were prepared by adding 20 wt% of dimension stone residue to the clay and sintered at 1000 °C for 1 h. The testing assays performed were physical properties and structural analysis through sc
Cerâmica. Publicado em: 2023
-
3. Microstructure and diametral fracture strength of spark plasma sintered WC-6Co-0.2B and WC-6Co-0.5B ceramic composites from nanosized and metastable WC powders
Abstract The present work aimed at evaluating the microstructures and mechanical properties of spark plasma sintered WC-6 wt% Co ceramic composites doped with boron (0.2 and 0.5 wt%). W-50 at% C (W-6.13 wt% C) powders produced under different milling times (20, 60, 180, and 600 min) were used as starting materials and subsequently mixed with Co (6 wt%) and B
Cerâmica. Publicado em: 2022
-
4. Gas permeability and compressive strength evaluation of porous Al2O3 supported membrane
Abstract The aim was to investigate the feasibility of using a device to characterize permeability in porous substrates with low gas flux. Al2O3 supports were prepared by dry pressing using 1 to 3 wt% of polyethylene glycol (PEG) as a pore-forming agent. The green body was partially sintered at 1300 ºC. CO2 gas was used to measure both the pressure loss and
Cerâmica. Publicado em: 2022
-
5. Effects of plaster to water ratio on physical and mechanical properties of ceramic pieces produced by the slip casting process
Abstract In the slip casting process, the relationship between the amount of plaster and water used in the production of molds influences the production of ceramic materials, because the higher the water content in the mixture, the lower the mechanical strength of the mold and higher the water absorption rate. In order to evaluate the influence of the variat
Cerâmica. Publicado em: 2022
-
6. Silicon carbide hollow fiber membranes developed for the textile industry wastewater treatment
Abstract In order to reduce the impacts of the industrial effluent on the environment, silicon carbide hollow fiber membranes were prepared by the precipitation-immersion technique and sintered at 1450 and 1500 °C. The membranes were characterized by X-ray diffraction, their surface structure was characterized by scanning electron microscopy and atomic forc
Cerâmica. Publicado em: 2021-06
-
7. Dolomite-zirconia reaction sintered bonded coarse magnesia ceramics: effect of the bonding proportion
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Cerâmica. Publicado em: 2021-06
-
8. Editorial Comment: Luts-V: A new simplified score for assessing lower urinary tract symptoms in men
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
9. Oxidative Stress & Male Infertility - A necessary and conflicted indissociable marriage: How and when to call for evaluation?
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
10. Editorial Comment: Vasectomy re-reversal: effectiveness and parameters associated with its success
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
11. Dysplasia of the fibrous sheath with axonemal and centriolar defects combined with lack of mitochondrial activity as associated factors of ICSI failure in primary ciliary dyskinesia syndrome
Abstract Refractory ceramic materials were manufactured, mainly composed of magnesia grains (coarse and medium fraction) and CaZrO3/MgO as a binding phase produced from the reaction sintering between CaMg(CO3)2 (dolomite) and m-ZrO2 (monoclinic zirconia), which constituted the finer fraction. Different relationships between the proportion and the size of the
Int. braz j urol.. Publicado em: 2021-06
-
12. Influence of sintering parameters on the microstructure and mechanical properties of nanosized 3Y-TZP ceramics
Abstract The fracture toughness of 3Y-TZP ceramics obtained from a nanocrystalline powder with an optimized microstructure and highly transformable tetragonal grains was investigated. Samples of ZrO2-3 mol% Y2O3 were sintered at temperatures between 1250 and 1400 °C, with isothermal holding times of up to 16 h. Samples sintered at 1250 °C exhibited relativ
Cerâmica. Publicado em: 2021-03