1. Bioactive SiO2-K2O-CaO-P2O5 glass-ceramic scaffold prepared using polyurethane foam template
Abstract A glass-ceramic in the SiO2-K2O-CaO-P2O5 quaternary system was prepared by substituting the Na2O component with K2O to avoid Na2Ca2Si3O9 formation upon thermal treatment since this phase decreases apatite formation kinetics on glass material. To form the glass-ceramic, a modified sol-gel method involving solution precipitation, followed by reagents
Cerâmica. Publicado em: 2023
-
2. Effect of a Bioactive Glass Ceramic on the Control of Enamel and Dentin Erosion Lesions
Resumo Este estudo avaliou o efeito de uma vitrocerâmica bioativa para o controle de lesões de erosão e cárie. Fragmentos (n=10) de esmalte bovino e dentina radicular receberam aplicação diária de diferentes tratamentos (Biosilicato; Fluoreto de Fosfato Acidulado - APF; não tratado - controle) durante a realização de ciclos erosivos. As superfície
Braz. Dent. J.. Publicado em: 2017-08
-
3. Bioactivity of leucite containing glass - ceramics using natural raw materials
Glass compositions were carefully prepared, using natural quartz and potassium feldspar as a part of the starting raw materials. The solids were prepared so as to have theoretical stoichiometric leucite and 45S5 Bioglass in different L/Bg weight ratios between 0.43 - 1.00. Novel bioactive glass - ceramics, containing leucite, sodium calcium silicate and sili
Mat. Res.. Publicado em: 22/07/2014
-
4. In vitro osteoblastic differentiation on bioactive glass and glassceramic surfaces / Análise da diferenciação osteoblástica in vitro sobre superfícies de materiais vítreos e vitrocerâmicos bioativos
Materiais vítreos e vitrocerâmicos bioativos podem ser usados particulados ou como scaffolds em diferentes tratamentos de defeitos ósseos. Tratamentos térmicos que possibilitam o desenvolvimento de scaffolds a partir de composições de vidros bioativos introduzem fases cristalinas em sua estrutura amorfa com potencial impacto na bioatividade e biocompat
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 17/08/2012
-
5. Avaliação de cimentos de ionômero de vidro modificados por resina frente à incorporação de nanopartículas de vitrocerâmica bioativa / Resin modified glass ionomer cements evaluation with additional bioactive glass-ceramics nanoparticles
Os materiais bioativos são materiais sintéticos que possuem superfícies ativas em que os minerais presentes em tecidos duros podem se ligar quimicamente. Há alguns estudos em Odontologia, onde partículas desses materiais foram incorporadas aos Cimentos de Ionômero de Vidro (CIVs) e Cimentos de Ionômero de Vidro modificados por resina (CIVMRs) com o ob
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 31/05/2011
-
6. Biosilicato®: histórico de uma vitrocerâmica brasileira de elevada bioatividade
This paper presents a historical of the Biosilicate®, a bioactive glass-ceramic developed at the Vitreous Materials Laboratory of the Federal University of São Carlos, Brazil. After decades of study accomplished with bioactive glasses and glass-ceramics, Biosilicate® results from a natural evolution and has similar bioactivity index, but far superior mech
Química Nova. Publicado em: 2011
-
7. A novel bioactive glass-ceramic for treating dentin hypersensitivity
Dentin hypersensitivity (DH) is a painful response to stimulus applied to the open dentinal tubules of a vital tooth. It's a common oral condition, however, without an ideal treatment available yet. This work evaluated in vitro the effect of micron-sized particles from a novel bioactive glass-ceramic (Biosilicate) in occluding open dentinal tubules. A dentin
Brazilian Oral Research. Publicado em: 2010-12
-
8. Processamento e caracterização de espumas vitrocerâmicas do sistema sncp (Sio2-Na2o-Cao-P2 O5)
Glass-ceramics foams prepared from glasses of the SiO2-Na2O-CaO-P2O5 by replication process were obtained and characterized in terms of their chemical and physical properties by X-ray fluorescence, X-ray diffraction, laser diffraction, thermal analysis, density, mechanical strength, microstructural and cytotoxic analysis. The results showed that it is possib
Química Nova. Publicado em: 2010
-
9. Avaliação da resistência de união de um cimento resinoso a um filme vitrocerâmico depositado em superfície de Y-TZP / Evaluation of bond strength of a resin cement to ceramic film deposited on a surface Y-TZP
The use of Y-TZP for dental ceramics strengthening has expanded significantly its mechanical properties, allowing its use in various clinical situations such as intraradicular, crowns, fixed partial dentures and implants. With the development of these new ceramic systems the use of traditional methods for surface treatment have been observed to be ineffectiv
Publicado em: 2010
-
10. Properties and adhesion of glass ionomer cements modified by resin and bioactive glass-ceramic / Propriedades e adesão de cimentos de ionômero de vidro modificados por resina e vitrocerâmicas bioativas
Bioactive glass-ceramics are synthetic materials capable of chemically bonding to dental structures. Adhesion of resin-modified glass-ionomer cements (RMGICs) to dentin may be influenced by different types of dentin pre-treatments. The objective of this study was to analyze the compressive strength, roughness and adhesion to dentin of RMGICs (Fuji II LC and
Publicado em: 2009
-
11. Potencial osteogênico in vivo de uma nova vitrocerâmica bioativa (Biosilicato)
Bioactive materials have the ability to bond and to integrate with bone tissue by forming a biologically active bonelike apatite layer, which has chemical and structural properties equivalent to the mineral phase of living bone. This process is determined by chemical reactions, whose products also influence the attachment, the proliferation, the differentiat
Publicado em: 2009
-
12. Bone formation on Ti implants in intra-bony defect sites filled with different bone substitutes: histomorphometric analysis in dogs / Avaliação clínica, histológica e histomorfométrica do reparo de defeitos ósseos criados em mandíbula de cães preenchidos com Biovidro 45S5 ou Biosilicato® após a colocação de implantes osseointegráveis
O presente trabalho avaliou a formacao de tecido osseo ao redor de implantes osseointegraveis de titanio, apos realizacao de defeitos osseos, utilizando diferentes tipos de substitutos osseos. Foram utilizados 5 caes de raca indeterminada, os pre molares e molares mandibulares foram extraidos, passados 12 semanas, os caes foram submetidos a um novo procedime
Publicado em: 2008