1. Estudio del comportamiento de fundición CADI sometida a FCR
ABSTRACT Ductile Iron (DI) is a development of the iron alloys introduced in the ´50s, with free graphite in the form of nodules. Austempered Ductile Iron (ADI) is a development of DI later introduced, consisting on austempering heat treatment in order to obtain a high strength and high toughness material. Carbidic Austempered Ductile Iron (CADI) is a more
Matéria (Rio J.). Publicado em: 19/07/2018
-
2. Estabilidad de la austenita retenida bajo condiciones de deformación en aceros multifásicos con bainita nanoestructurada
ABSTRACT A steel with nominal composition 0.25C, 1.9Si, 0.63Mn, 1.5Cr was manufactured using an induction furnace. The as-cast alloy was homogenized and the temperatures of austenite start (AC1) and finish (AC3) during heating were determined by dilatometric analyses. Two intercritical austenitization temperatures were selected, which were used to perform pa
Matéria (Rio J.). Publicado em: 19/07/2018
-
3. Determinación de los parámetros de austenización intercrítica para el desarrollo de aceros multifásicos mediante análisis dilatométrico
ABSTRACT The Multiphase steels are materials with exceptional mechanical properties including high strength, excellent ductility and hardening coefficient and good conformability. These properties are related with the microstructure, which can be a combination of ferrite and martensite (Dual phase steels) or more complex microstructures with ferrite, bainite
Matéria (Rio J.). Publicado em: 19/07/2018
-
4. Boro-Austempering Treatment of Ductile Cast Irons
Samples of ductile cast irons alloyed with Cu, Cu-Ni and Cu-Ni-Mo were austempered, borided and boro-austempered and characterized for hardness and micro-adhesive wear behavior. The kinetics of layer formation was also studied. The boriding method used was molten borax bath, in periods of 2 and 4 hours at temperatures of 850, 900 and 950 ºC. The direct aust
Mat. Res.. Publicado em: 16/07/2018
-
5. Design of the austempering heat treatment of a ductile iron differential case aided by computer simulation
Abstract Austempered ductile iron is frequently employed in the fabrication of automobile parts due to its good mechanical properties, and its simplicity and low cost of the manufacturing process. The heat treatment design is an important stage, in which parameters such as temperatures and durations are chosen according to the required microstructure, part
Lat. Am. j. solids struct.. Publicado em: 02/07/2018
-
6. Effect of Heat Treatments and SiC Content in the Mechanical Properties and Microstructure of Self-Lubricating Steels
The objective of the present work was to study the effect of heat treatments in the microstructure, graphite nodules and mechanical properties of self-lubricating steels, to achieve this, self-lubricating steels (Fe + 0.45C + 4Ni + 1Mo %wt) and additions of 2 and 3 %wt SiC were fabricated. They were consequently heat treated in 3 different conditions: martem
Mat. Res.. Publicado em: 09/11/2017
-
7. Influence of casting heterogeneities on microstructure and mechanical properties of austempered ductile iron (ADI)
ABSTRACT An investigation was carried out to examine the influence of as-cast heterogeneities on the resulting microstructure and mechanical properties of an austempered ductile cast iron (ADI). A commercial hypereutectic ductile iron alloy with 3.59% C, 2.68% Si, 0.24% Mn and 0.46% Cu (in wt. %) was produced in a coreless induction furnace. The specimens we
Matéria (Rio J.). Publicado em: 10/08/2017
-
8. Estudo dos mecanismos de fadiga e análise de desempenho em mola para válvula automotiva em regime de alto e ultra-alto ciclo. / Study on the fatigue mechanisms and performance analysis in automotive valve spring under high-and-ultra-high-cycle regime.
This paper presents a study on the valve spring fatigue mechanisms, carried out through analysis of mechanical behavior correlated to microstructural aspect. The samples were made of high strength steel Si-Cr, obtained by conventional (quenching and tempering) and unconventional (austempering) heat treatments, generating a single level of hardness (approxima
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 05/03/2012
-
9. Análise comparativa do efeito da têmpera e revenimento e da austêmpera seguida ou não de conformação a frio na microestrutura e nas propriedades do aço SAE 4140H / Comparative analysis of the effect of the quench and tempering and the austempering followed or not by cold forming in the microstructure and in the steel properties SAE 4140H
O objetivo deste trabalho é analisar a possibilidade de substituição do tratamento térmico de têmpera e revenimento pelo tratamento térmico de austêmpera, seguido ou não de conformação plástica a frio, na fabricação de barras laminadas do aço SAE 4140H. A temperatura de austenitização, para ambos os tratamentos, foi de 850ºC, com tempo de en
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 08/09/2011
-
10. Influência da deformação superficial induzida na resistência à fadiga do ferro fundido nodular austemperado
The austempered ductile iron (ADI) is stronger, lighter and cheaper than forged carbon steels. In addition, ADI displays a higher ductility, toughness and resistance to wear than other cast irons. This work presents an analysis of the effect of induced superficial deformation on the fatigue resistance of ADI and it was studied the possibility to reduce the t
Publicado em: 2010
-
11. Estudo da influência das temperaturas de austenitização nas propriedades mecânicas do ferro nodular austemperado a partir da zona crítica
In the present work the influence of austenitizing temperature on mechanical properties Austempered Ductile Iron from intercritical austenitizing temperature ranges was investigated. A heat treatment for development of material with improved mechanical properties for application in suspension parts is shown. Samples of alloyed ductile iron with a fully ferri
Publicado em: 2009
-
12. Influência dos elementos de liga Cu-Ni-Mo nas propriedades mecânicas e na austemperabilidade do ADI / Influence of alloys elements Cu-Ni-Mo on mechanical properties and austemperability of ADI.
O ADI constitui-se no desenvolvimento mais recente na família dos ferros fundidos nodulares. Com o tratamento de austêmpera, consegue-se produzir uma microestrutura única, constituída de ferrita acicular e austenita estável rica em carbono, a ausferrita, proporcionando alta resistência mecânica aliada à ductilidade e tenacidade, além de boa resistê
Publicado em: 2009