Ultra baixo coeficiente de atrito no deslizamento de Si3N4-Al2O3. Efeitos da força aplicada, velocidade de deslizamento e temperatura do ensaio. / Ultra low friction coefficient in sliding of Si3N4-Al2O3. Effects of applied load, sliding velocity and test temperature.
AUTOR(ES)
Eliel dos Santos Paes
FONTE
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia
DATA DE PUBLICAÇÃO
27/02/2012
RESUMO
Tribological tests were conducted in a ball on disk setup, using water as lubricant. Were used a silicon nitride ball and alumina disk. The tests were conducted to investigate the effects of sliding speed, applied load and temperature on friction coefficient. The silicon nitride balls and alumina disks were characterized by determining density, Vickers hardness, elastic modulus and fracture toughness. The tests were conducted with initial roughness on the disk surface of 352 nm. The ultra low friction coefficient regime (ULFC, μ <0.01) was reached after a running-in period of approximately one hour and the friction coefficient remains in the range of μ = 0.008 a μ = 0.002 during this steady state regime. The results showed that this sliding system has hydrodynamic characteristics, because the friction coefficient decreased with increasing of the sliding speed. With an smooth variation of the applied load the system remained in the ULFC regime, when the applied load varied from 54 N up to 94 N. At temperatures below or equal to 11°C the system did not reach the ULFC regime and the final friction coefficient was the order of hundredths. We observed the ULFC phenomenon at temperatures of 30 and 40°C. However, at these temperatures, the water viscosity is low and should not allow the system to reach the ULFC regime. The data analysis allowed infer that during the ULFC regime the system slides with a mixed lubrication regime, hydrodynamic plus limitrofe, the first due to water film and the second due to the hydrated layer formed on the ceramics surfaces. The results showed a influences of temperature in the ceramics wear. The results of the worn volume allowed to observe that during the tests alumina suffers less wear than the silicon nitride, and the ceramics wear increases with increasing temperature.
ASSUNTO(S)
alumina alumina cerâmica ceramics desgaste lubrificação com água nitreto de silício silicon nitride ultra baixo coeficiente de atrito ultra low friction coefficient water lubrication wear
Documentos Relacionados
- Ultra-low friction coefficient between Si3N4-Al2O3 in water.
- Ultra baixo coeficiente de atrito no deslizamento de Al2O3 - Si3N4: efeito das variáveis químicas (pH e concentração de sílica coloidal).
- Si3N4 ceramic cutting tool sintered with CeO2 and Al2O3 additives with AlCrN coating
- Dispersão e comportamento reológico de concretos refratários ultra-baixo teor de cimento no sistema Al2O3-SiC-SiO2-C
- Evaluation of the reliability of Si3N4-Al2O3 -CTR2O3 ceramics through Weibull analysis