The effects of ZnO2 nanoparticles on properties of concrete using ground granulated blast furnace Slag as binder
AUTOR(ES)
Nazari, Ali, Riahi, Shadi
FONTE
Materials Research
DATA DE PUBLICAÇÃO
12/08/2011
RESUMO
In the present study, flexural strength together with pore structure, thermal behavior and microstructure of concrete containing ground granulated blast furnace slag with different amount of ZnO2 nanoparticles has been investigated. Portland cement was replaced by different amounts of ground granulated blast furnace slag and the properties of concrete specimens were investigated. Although it negatively impact the properties of concrete, ground granulated blast furnace slag was found to improve the physical and mechanical properties of concrete up to 45 wt. (%). ZnO2 nanoparticles with the average particle size of 15 nm were added partially to concrete with the optimum content of 45 wt. (%) of ground granulated blast furnace slag and physical and mechanical properties of the specimens was measured. ZnO2 nanoparticle as a partial replacement of cement up to 3 wt. (%) could accelerate C-S-H gel formation as a result of increased crystalline Ca(OH)2 amount at the early age of hydration and hence increase flexural strength of concrete. The increased the ZnO2 nanoparticles' content more than 3 wt. (%), causes the reduced the flexural strength because of the decreased crystalline Ca(OH)2 content required for C-S-H gel formation together with unsuitable dispersion of nanoparticles in the concrete matrix. ZnO2 nanoparticles could improve the pore structure of concrete and shift the distributed pores to harmless and few-harm pores.
Documentos Relacionados
- Prediction the effects of ZnO2 nanoparticles on splitting tensile strength and water absorption of high strength concrete
- The Effects of ZnO2 nanoparticles on strength assessments and water permeability of concrete in different curing media
- The effects of CuO nanoparticles on properties of self compacting concrete with GGBFS as binder
- Application of biosynthesized ZnO nanoparticles on an electrochemical H 2 O 2 biosensor
- Effects of precursor concentration and reaction time on sonochemically synthesized ZnO nanoparticles