Study of the aluminothermic reduction of niobium pentoxide through thermal analysis experiments and high energy milling processing
AUTOR(ES)
De Lazzari, Claudio Parra, Simões, Danielle Goya, Capocchi, José Deodoro Trani
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2007-06
RESUMO
Aluminothermic reduction of niobium pentoxide was studied through thermal analysis techniques such as differential thermal analysis (DTA) and thermogravimetry (TG) as well as through high energy milling processing. Reactants mixtures were composed by powders of Nb2O5 and Al. In the case of DTA-TG experiments, different molar ratios Nb2O5:Al were heated in a dynamic atmosphere of synthetic air under controlled conditions. The high energy milling runs were carried out via SPEX vibratory mill under argon atmosphere and with milling power equal to 7:1 (ratio of mass of balls to mass of mixture) with 10 pct excess of Al over the stoichiometric mass of aluminum necessary. In both kinds of experiments, X ray diffraction was used in order to identify the products of reaction. From DTA-TG experiments, it was possible to determine the experimental value of the enthalpy change (-595.9 kJ.mol-1), which is near to the theoretical one. From the milling experiments, it was possible to verify the possibility of the occurance of aluminothermic reducion of niobium pentoxide via this kind of processing.
Documentos Relacionados
- Evaluation of the milling efficiency increase of AISI 52100 steel using niobium carbide addition through high energy ball milling
- Comparative analysis of niobium and vanadium carbide efficiency in the high energy mechanical milling of aluminum bronze alloy
- Study of the AISI 52100 Steel Reuse Through the Powder Metallurgy Route Using High Energy Ball Milling
- Effect of High Energy Milling Time of the Aluminum Bronze Alloy Obtained by Powder Metallurgy with Niobium Carbide Addition
- Characterization of ZSM-5 modified with niobium pentoxide: the study of thiophene adsorption