Study of Structural and Electric Properties of the PZT 52/48 Doped With Er+3
AUTOR(ES)
Caceres, Jaime Alberto Sanchez
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
25/11/2019
RESUMO
The scientific community has shown a growing interest in relating to the ferroelectric materials and it has made an effort to develop them. Among these several ferroelectric materials, we proposed to investigated Pb(ZrTi)O3 doped with distinct Er+3 concentrations. Our aim was to investigate how the erbium affects the PZT electrical properties. To determine the ideal sintering temperature of our ceramic samples, the dilatometry tests were performed. These results have showed that the erbium caused a change in sample densities (91.9% < ρ < 99.0%) as compared to undoped PZT sample. Furthermore, the X-ray diffraction results indicated that all samples are monophasic and peaks are indexed to tetragonal crystalline structure. According to these also results, there was an increment of the parameter a and a reduction of parameter c as compared to undoped PZT sample. On the other hand, the average grain size have decreased with the increment of erbium content. The electrical characterization of ours ceramics showed a peculiar ferrelectric-paraeletric phase transition around 390 ºC. Finally, the ferroelectric hysteresis measurements for doped samples in site A have revealed that remnant polarization and coercive field values depend on content. Whereas, doped samples in site B, the corresponding values are similar.
Documentos Relacionados
- Structural Evolution and Electrical Properties of BaTiO3 Doped with Gd3+
- Comportamento óptico estrutural da zircônia dopada com Er3+,Pr3+ e estabilizante de fase Y3+
- Influence of the crystallization thermal treatment on the structural and electrical properties of PZT thin films
- Properties and structural features of iron doped BABAL glasses
- Structural, optical and electrical properties of Ni-doped Co3O4 prepared via Sol-Gel technique