Study of photoinduced birefrigence, in layer-by-layer films containing azopolymer and azodye / Estudo de birrefrigência fotoinduzida em filmes automontados de azopolímeros e azocorantes

AUTOR(ES)
DATA DE PUBLICAÇÃO

2005

RESUMO

This work was aimed at investigating the influence of the molecular architecture and film fabrication on the photoinduced birefi-ingence of layer-by-layer (LbL) films containing the azopolymer PS 119® or the azodye Brylliant Yellow (BY) as photoreactive materials. The LbL films were produced with six polications, viz.: poly(allylamine hydrochloride) (PAH), poly(diallyldimethylammonium chloride) (PDAC) (with three different molecular weights), poly(ethy1eneimine) (PEI) and generation 4 dendrimer poly(amidoamine) (PAMAM-G4). They were prepared via the alternate immersion of a substrate into the polycationic and polyanionic aqueous solutions, at concentrations of 0.5 mg/mL at three pHs: 4, 6 and 8. The assembly of multilayers was monitored aRer each adsorption step by UV-VIS spectroscopy. A linear increase was observed in the peak at 480 nm, assigned to the transition of the azobenzene moiety, indicating that the same amount of material was deposited at each deposition step. Birefringence was optically induced in films using a 532 nm NdYAG laser. Among the LbL properties, the characteristic writing time - corresponding to the time to achieve 50% of maximum birefiingence - was the quantity that most varied with the materials and experimental conditions employed. The writing time was estimated as 34 min. for PEI/PS-119 with solution at pH 8 films, 0.5 min. for PDAC(HMW)/PS-119, pH 4 films, ca. 10 min. for PAWBY, pH 8 films and 3 s for PDAC(HMW)íBY, pH 4 films. These differences in writing times are probably related to the structural differences of the polycations, which determine the degree of interactions between polycation and polyanion. Indeed, interactions between polyanion and PDAC are expected to occur to a lesser extent (in comparison to the other films) due to the hindering promoted by the dimethyl group in the quaternary ammonium salt, minimizing the interaction with sulfonated groups from PS-119 or BY. With less interaction the azobenzene groups are more mobile, thus causing the writing time to be shorter for PDACIpolyanion films. It should be stressed that the writing time for PDAC/BY is the shortest ever reported for LbL films, being of the same order of magnitude of writing times in cast and Langmuir-Blodgett (LB) films. The residual birefringence, aRer the writing laser was switched off, was at least 78% for all systems, indicating that these LbL films are suitable for long-term optical memories.

ASSUNTO(S)

azocorante birefrigence azodye photoinduced filme automantado azopolímero birrifrigência fotoinduzida layer-by-layer films azopolymer

ACESSO AO ARTIGO

Documentos Relacionados