Sinterabilidade de pós de precursor vitrocerâmico do sistema LZSA tratados por troca iônica
AUTOR(ES)
Montedo, Oscar Rubem Klegues, Ronsani, Patrícia, Oliveira, Antonio Pedro Novaes de
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2012
RESUMO
Ion exchange method was employed by means of surface modification of the glass powders of LZSA (Li2O-ZrO2-SiO2-Al2O3) system submitted to a 70wt% NaNO3/30wt% NaSO4 bath salt followed by a heat treatment. Chemical analysis by X-ray fluorescence was used to evaluate the efficiency of ion exchange, while optical dilatometry was employed to evaluate sintering of compacts. Evaluation of the structure of sintered bodies was made by scanning electron microscopy. Substitution of Li+ ions by Na+ ions on the surface of powders during heat treatments of 450 and 600 ºC for 2-10 h promoted an increase in densification of the sintered bodies.
Documentos Relacionados
- Estudo de composições cerâmicas à base de alumina e vitrocerâmico do sistema LZSA para obtenção de estruturas multicamadas por tape casting
- Reação em estado sólido em compósitos alumina nanoparticulada/vitrocerâmico LZSA
- Purificação de albumina humana por cromatografia de troca ionica para estudos imunoquimicos
- Modelo matemático do processo de purificação do ácido clavulânico por troca iônica em coluna de leito fixo
- Reologia de suspensões de precursor vitrocerâmico do sistema LiO2-ZrO2-SiO2-Al2O3