Push-out bond strength of different tricalcium silicate-based filling materials to root dentin
AUTOR(ES)
Stefaneli Marques, Jorge Henrique, Silva-Sousa, Yara Teresinha Corrêa, Rached-Júnior, Fuad Jacob Abi, Macedo, Luciana Martins Domingues de, Mazzi-Chaves, Jardel Francisco, Camilleri, Josette, Sousa-Neto, Manoel Damião
FONTE
Braz. oral res.
DATA DE PUBLICAÇÃO
08/03/2018
RESUMO
Abstract: The aim of this study was to evaluate the bond strength of different triccalcium silicate cements to retrograde cavity using a push out test. Thirty maxillary central incisors were shaped using #80 hand files and sectioned transversally. Root slices were obtained from the apical 4 mm after eliminating the apical extremity. The specimens were embedded in acrylic resin and positioned at 45° to the horizontal plane for preparation of root-end cavities with a diamond ultrasonic retrotip. The samples were divided into three groups according to the root-end filling material (n = 10): MTA Angelus, ProRoot MTA and Biodentine. A gutta-percha cone (#80) was tugged-back at the limit between the canal and the root-end cavity. The root-end cavity was filled and the gutta-percha cone was removed after complete setting of the materials. The specimens were placed in an Instron machine with the root-end filling turned downwards. The push-out shaft was inserted in the space previously occupied by the gutta-percha cone and push out testing was performed at a crosshead speed of 1.0 mm/min. There was no statistically significant difference in resistance to push out by the materials tested (p > 0.01). MTA Angelus and ProRoot MTA showed predominantly mixed failure while Biodentine exhibited mixed and cohesive failures. The tricalcium silicate-based root-end filling materials showed similar bond strength retrograde cavity.
Documentos Relacionados
- Push-out bond strength of MTA HP, a new high-plasticity calcium silicate-based cement
- Push-out Bond Strength of Root-end Filling Materials
- Bond strength of different endodontic sealers to dentin: push-out test
- Apical adaptation, sealing ability and push-out bond strength of five root-end filling materials
- Physicochemical Properties and Dentin Bond Strength of a Tricalcium Silicate-Based Retrograde Material