Produção e caracterização de espumas cerâmicas obtidas a partir de lodo de anodização de alumínio
AUTOR(ES)
Moraes, Graziela Guzi de, Rodrigues Neto, João Batista, Hotza, Dachamir, Oliveira, Antonio Pedro Novaes de, Oliveira, Bianca Goulart de, Oliveira, Therezinha Maria Novais de
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2012
RESUMO
Ceramic foams were produced from a sludge generated in the aluminum anodizing process by using an industrial polyurethane foam (replication method) with open cell sizes of 10 ± 5 ppi (porosity = 97%) which were impregnated with suspensions containing 50-61 wt.% alumina, 1 wt.% citric acid, 6 wt.% bentonite and fired at 1600 ºC for 2 h. The aluminum anodizing sludge shows a high alumina content (87.5 wt.%) and a low particle size (~1.7 mm) after calcination and milling. The obtained filters show porosity of approximately 70%, filtration capability (mass water flow) of 1.7 kg/s and mechanical strength under compression of 2.40 MPa.
Documentos Relacionados
- Produção e caracterização de espumas vitrocristalinas a partir de resíduos sólidos
- Obtenção e caracterização de espumas cerâmicas de alumina para uso como queimadores radiantes
- Obtenção de espumas cerâmicas a partir de resíduo da terra diatomácea e ignimbrita pelo método de réplica
- Avaliação da perda de massa de farinhas precursoras de clínquer CSAB compostas com lodo de anodização do alumínio
- Defloculação de massas cerâmicas triaxiais obtidas a partir do delineamento de misturas