Mechanical characterisation of porous glass reinforced hydroxyapatite ceramics: Bonelike®
AUTOR(ES)
Silva, Marcelo Henrique Prado da, Lemos, Alexandra Fernandes, Ferreira, José Maria da Fonte, Santos, José Domingos
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2003-06
RESUMO
In the present study, mechanical properties of porous glass reinforced hydroxyapatite bioceramics were assessed by microhardness, bending and compression tests and fracture toughness determination. Porous discs were produced by a dry method using wax spheres as pore formers. Green bodies were sintered and the final microstructure of the composites consists of hydroxyapatite, alpha and beta tricalcium phosphate (alpha and b-Ca3(PO4)2)due to the reaction between the glassy phase and the hydroxyapatite matrix. The results of the mechanical tests showed that the glassy phase yielded higher fracture toughness and bending strength when comparing with literature data for single hydroxyapatite. There is a compromise between mechanical properties and the porosity level for bioceramics: for example, according to Weibull statistics for composites with 65% porosity the maximum bending stress level is 0.2 MPa for 100% survival probability whereas this stress level increases to 2.5 MPa for composites with 40%. However, only the 65% porosity composite samples seem to have the complete adequate morphology for bone ingrowth.
Documentos Relacionados
- Mechanical Properties of Glass Fiber Reinforced Polymers Members for Structural Applications
- Reinforced Glass-ceramics: Parametric Inspection of Three-Dimensional Wear and Volumetric Loss after Chewing Simulation
- Mechanical properties and porosity of dental glass-ceramics hot-pressed at different temperatures
- Dental ceramics: a review of new materials and processing methods
- Incorporation of solid wastes in red ceramics: an updated review