Kinetics of sigma phase formation in a Duplex Stainless Steel
AUTOR(ES)
Magnabosco, Rodrigo
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2009-09
RESUMO
This work determines the kinetics of sigma phase formation in UNS S31803 Duplex Stainless Steel (DSS), describing the phase transformations that occur in isothermal aging between 700 and 900 ºC for time periods up to 1032 hours, allowing the determination of the Time-Temperature-Precipitation (TTP) diagram for sigma phase and proposing a model to predict the kinetics of sigma phase formation using a Johnson-Mehl-Avrami (JMA) type expression. The higher kinetics of sigma phase formation occurs at 850 ºC. However, isothermal aging between 700 and 900 ºC for time periods up to 1032 hours are not sufficient to the establishment of thermodynamic equilibrium. Activation energy for both nucleation and growth of sigma phase is determined (185 kJ.mol-1) and its value is equivalent to the activation energy for Cr diffusion in ferrite, indicating that diffusion of Cr is probably the major thermally activated process involved in sigma phase formation. The determined JMA type expression presents good fit with experimental data between 700 and 850 ºC.
Documentos Relacionados
- Sigma Phase in Superduplex Stainless Steel: Formation, Kinetics and Microstructural Path
- Use of Magnetic Barkhausen Noise (MBN) to Follow Up the Formation of Sigma Phase in Saf2205 (UNS S31803) Duplex Stainless Steel
- Effect of Sigma Phase Precipitated at 850 °C on Corrosion Behaviour of UNS S82441 Duplex Stainless Steel
- A New methodology of Nondestructive Testing for Quantitative Evaluation of Sigma Phase in Duplex Stainless Steels
- On the Nitrogen Diffusion in a Duplex Stainless Steel