Influencia de la temperatura de curado: hidratación y resistencia de pastas de cemento con escoria
AUTOR(ES)
Castellano, C. C., Bonavetti, V. L., Irassar, E. F.
FONTE
Matéria (Rio de Janeiro)
DATA DE PUBLICAÇÃO
2010
RESUMO
Nowadays it is well known that using blast furnace slag as partial replacements for Portland cement adds technological, economic and environmental benefits. Those are some of the reasons why cements containing several additions (blast furnace slag, fly ash, calcareous material, etc) are commonly used. In recent years, blended cements started to increase amounts of additions as replacement of Portland cement; in this regard these variations influence the rate and the mechanism of hydration and, consequently, strength development. The present work evaluated the effect of different curing temperatures (20, 40 and 60 ºC) on the mechanical strength of cement paste with different proportions of granulated blast-furnace slag (0 to 80 %). Pastes were prepared with water/cementitious material ratio (w/cm) equal to 0,4. The hydration evolution was determinated following the hydration products using XRD analysis and evaluated the content of non evaporable water. Mechanical strength was evaluated trough central composite experimental design. When granulated blast-furnace slag content increases with curing temperature, the results show that mechanical strength and non evaporable water increases, while the calcium hydroxide content decreases.
Documentos Relacionados
- Retracción química de pastas de cemento con incorporación de metacaolín
- Fundente para Recargue por Soldadura con Arco Sumergido a Partir de Ferrocromo-manganeso y Escoria de la Reducción Simultánea de Cromita y Pirolusita
- Métodos de determinación de la cinética de hidratación mediante la retracción química y parámetros que lo influencian
- Influencia del proceso de curado y del contenido de carga sobre la Tg y el volumen libre en compuestos particulados de matriz epoxi
- Estudio cinético del efecto de polifenilsulfona sobre el curado de una resina epoxi/amina mediante calorimetría diferencial de barrido convencional y modulada con temperatura: parte II