Influence of Cavity Dimensions on Microleakage of Two Bulk-Fill Composite Resins
AUTOR(ES)
Naghili, Armaghan
FONTE
Pesqui. Bras. Odontopediatria Clín. Integr.
DATA DE PUBLICAÇÃO
31/10/2019
RESUMO
Abstract Objective: To evaluate the effect of cavity dimensions on the amount of microleakage in two different types of bulk-fill composite resins. Material and Methods: Forty class II cavities were prepared in the mesial and distal surfaces of human molars without any carious lesions. The samples were divided into 4 groups (n=10): Group 1: cavities with 3 mm of buccolingual width (known as the smaller cavity), filled with Tetric N-Ceram Bulk Fill composite resin; Group 2: cavities with 6 mm of buccolingual width (larger cavity), filled with Tetric N-Ceram Bulk Fill composite resin; Group 3: cavities with 3 mm of buccolingual width, filled with X-Tra Base composite resin; and Group 4: cavities with 6 mm of buccolingual width, filled with X-Tra Base composite. After the specimens were thermocycled for 500 cycles at 5/55°C, they were immersed in 1% methylene blue for 24 hours, and then cut into sections mesiodistally in the longitudinal axis of each tooth. Then, the samples were scored regarding the amount of dye penetration in two occlusal and gingival areas under a stereomicroscope (x32). Data was submitted to Kruskal-Wallis and Mann-Whitney tests. Results: The highest degrees of microleakage in larger cavities filled with X-Tra Base among the four groups. There was a significant statistic difference (p=0.012) between large and small cavities filled with X-Tra Base (Groups 3 and 4); however, there was no significant difference between the two cavity sizes of Tetric N-Ceram Bulk-filled groups. Conclusion: Microleakage of composite resins depends on the dimension of the cavity and the type of composite resin used.
Documentos Relacionados
- Efficiency of polymerization of bulk-fill composite resins: a systematic review
- Effect of gastric acid on the surface roughness and bacterial adhesion of bulk-fill composite resins
- Physicomechanical characterization and biological evaluation of bulk-fill composite resin
- Interfacial Stress and Bond Strength of Bulk-Fill or Conventional Composite Resins to Dentin in Class II Restorations
- Development and characterization of a novel bulk-fill elastomeric temporary restorative composite