Evolución microestructural de un acero inoxidable superdúplex bajo ciclos térmicos de corta duración

AUTOR(ES)

Mendoza Bravo, Ivan, Maldonado Zepeda, Cuauhtémoc, Serrato Rodríguez, Juán, Albiter Hernández, Apolinar

FONTE

Soldagem & Inspeção

DATA DE PUBLICAÇÃO

2010-09

RESUMO

This work investigates the effect of thermal cycling on the microstructure of a stainless steel superduplex, specifically on the sigma phase formation. The examined thermal cycles are similar to those produced in the heat affected zone of stainless steel when applying GTAW welding process. The temperatures and residence time for the cycle was determined using a typical thermal model of temperature distribution. The application of thermal cycles shows the microstructural evolution of steel in the range of 475ºC to 1100ºC with a short heating time and determines the temperature of formation and disolution of the sigma phase, and its maximum temperature of formation. The formation mechanism and chemical composition of the sigma phase is also examined.

Documentos Relacionados

• Efecto de los ciclos térmicos sobre la ZAT de una soldadura multipasos de un acero inoxidable superdúplex SAF 2507
• Efecto del tiempo de superpulso de soldadura sobre la evolución microestructural de un acero de bajo carbono
• Estudio de la evolución microestructural durante el austenizado de un acero ASTMA335 P91
• Uso de técnicas electroquímicas para determinar la resistencia a la corrosión localizada de un acero inoxidable súper dúplex UNS S-32760
• Identificación de Fases y Precipitados por MFA en Uniones de Acero Inoxidable Dúplex