Electrospinning Preparation and Photoluminescence Properties of Y3Al5O12:Eu3+ Nanobelts
AUTOR(ES)
Bi, Fei, Dong, Xiangting, Wang, Jinxian, Liu, Guixia
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
2015-04
RESUMO
Novel structures of Y3Al5O12: Eu3+ (denoted as YAG: Eu3+ for short) nanobelts were fabricated by calcination of the electrospun PVP/[Y(NO3)3+Eu(NO3)3+Al(NO3)3] composite nanobelts. X-ray powder diffraction (XRD) analysis showed that YAG: Eu3+ nanobelts were cubic in structure with space group Ia3d. Fourier transform infrared spectroscopy (FTIR) analysis manifested that pure YAG: Eu3+ nanobelts were formed at 900 °C. Scanning electron microscope (SEM) analysis indicated that the YAG: Eu3+ nanobelts have coarse surface. The width and thickness of YAG: Eu3+ nanobelts were ca. 3.25 µm and ca. 220 nm, respectively. Fluorescence spectra analysis revealed that YAG: Eu3+ nanobelts emitted the main strong emission centering at 592 nm under the ultraviolet excitation of 235 nm, which was attributed to 5D0→7F1 of Eu3+, and the optimum doping molar concentration of Eu3+ ions was 5%. CIE analysis demonstrated that the emitting colors of YAG: Eu3+ nanobelts could be tuned by adjusting doping concentration of Eu3+. The possible formation mechanism of YAG: Eu3+ nanobelts was also proposed.
Documentos Relacionados
- PREPARATION AND PROPERTIES OF PT-RH-PD
- Photoluminescence properties of Te doped AlGaAsSb alloys
- Impact of fuel quantity on luminescence properties of Sr3Al2O6:Eu by combustion synthesis
- Properties of SiC Ceramics Sintered via Liquid Phase Using Al2O3 + Y2O3, Al2O3 + Yb2O3 and Al2O3 + Dy2O3 as Additives: a Comparative Study
- The preparation and properties of 4-thiouridine containing 2'-5' and 3'-5' dinucleoside monophosphates.