Effect of cariogenic challenge on the stability of dentin bonds
AUTOR(ES)
BORGES, Fernanda Blos, KOCHHANN DE LIMA, Ellen Luisa, MACHADO, Fernanda Wiengartner, BOSCATO, Noeli, VAN DE SANDE, Francoise Helene, MORAES, Rafael Ratto de, CENCI, Maximiliano Sergio
FONTE
J. Appl. Oral Sci.
DATA DE PUBLICAÇÃO
2014-01
RESUMO
Objective: The oral environment is subject to biofilm accumulation and cariogenic challenge, and few studies exist on the effect of these factors on the bond strength of adhesive systems. The aim of this study was to test if the exposure of adhesive interfaces to cariogenic challenge under biofilm accumulation could promote higher degradation than the exposure to biofilm accumulation alone. Material And Methods: Five molars were ground until exposure of medium dentin and then restored (Single Bond 2 and Z250 3M ESPE). The tooth/resin sets were cut to obtain beam-shaped specimens, which were distributed according to the aging conditions (n=20): water for 24 h (control); biofilm under cariogenic challenge for 3, 5 or 10 days; biofilm without cariogenic challenge for 10 days; and water for 3 months. Microcosm biofilms were formed from human saliva and grown in a saliva analogue medium, supplemented or not with sucrose to promote cariogenic challenge. Specimens were tested for microtensile bond strength, and failure modes were classified using light microscopy. Bond strength data were analyzed using ANOVA and failure modes were analyzed using ANOVA on ranks (α=0.05). Results: No significant differences in bond strength were detected among the aging methods (P=0.248). The aging period was associated with an increase in the frequency of adhesive failures for the groups aged for 10 days or longer (P<0.001). Conclusion: Aging leads to a higher prevalence of interfacial adhesive failures, although this effect is not associated with cariogenic challenge or reduction in bond strengths.
Documentos Relacionados
- Influence of Cariogenic Challenge on Bond Strength Stability of Dentin
- Effect of Cariogenic Challenge on the Degradation of Adhesive-Dentin Interfaces
- Effectiveness of plant-derived proanthocyanidins on demineralization on enamel and dentin under artificial cariogenic challenge
- Effect of Fluoride Concentration on Reduction of Enamel Demineralization According to the Cariogenic Challenge
- Effect of Erosion/Abrasion Challenge on the Dentin Tubule Occlusion Using Different Desensitizing Agents