Contribution to study effects of the turning operations in the surface integrity in a super duplex stainless steel. / Contribuição ao estudo da integridade superficial de um aço inoxidável super-duplex após usinagem.
AUTOR(ES)
Éd Claudio Bordinassi
DATA DE PUBLICAÇÃO
2006
RESUMO
The objective of this work was to study the effects of the turning operations in the surface integrity in a super duplex stainless steel (SDSS) ASTM A890-Gr6A. The focus of the work was the finishing operations but some tests in rough operations were carried out. A complete factorial planning was used for both, with 2 levels and 5 factors. The tests were conducted on turning centers with carbide tools and the main input variables were: tool geometry / tool material class, feed rate, cutting depth, cutting speed and the cutting fluid utilization. The analyzed answers were: microstructure analysis by optical microscopy and x-ray diffraction, cutting measurements by a piezoelectric dynamometer, surface roughness, micro-hardness, residual stress by x-ray diffraction technique and dimensional stability. The results do not showed any changes in the microstructure of the material, even when the greater cutting values were used. All the other answers were correlated with the cutting parameters and the best combination of cutting parameters was founded for the best surface integrity. The smaller feed rate (0,1mm/v), smaller cutting speed (110m/min) and greater cutting depth (0,5mm) provided the smaller values for the tension residual stress, the smaller roughness and the greater micro-hardness. The correlation between all the answers was very difficult to analyze because there was great interaction between the factors, but for some data groups it was possible.
ASSUNTO(S)
tensão residual usinagem aço inoxidável superduplex acabamento de superfícies surface integrity turning duplex stainless steel residual stress torneamento machining
Documentos Relacionados
- Effects of the machining in the surface integrity on the superaustenitic stainless steel
- Desenvolvimento do aço inoxidável super-duplex UNS S 32760 produzido em barras laminadas de grande diâmetro
- Relações de orientação resultantes da precipitação de austenita em ferrita em aço inoxidável dúplex.
- Estudo da integridade superficial e seu efeito na fadiga de contato de um aço ferramenta.
- The UNS S32520 superduplex stainless steel processing by mechanical alloying