Caracterização textural e estrutural de V2O5/TiO2 obtidos via sol-gel: comparação entre secagem convencional e supercrítica

AUTOR(ES)

Rodella, Cristiane B., Nunes, Luis A. O., Saeki, Margarida J., Padilha, Pedro M., Florentino, Ariovaldo O.

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2002-05

RESUMO

This work describes a modified sol-gel method for the preparation of V2O5/TiO2 catalysts. The samples have been characterized by N2 adsorption at 77K, x-ray diffractometry (XRD) and Fourier Transform Infrared (FT-IR). The surface area increases with the vanadia loading from 24 m² g-1, for pure TiO2, to 87 m² g-1 for 9wt.% of V2O5. The rutile form is predominant for pure TiO2 but became enriched with anatase phase when vanadia loading is increased. No crystalline V2O5 phase was observed in the catalysts diffractograms. Two species of surface vanadium observed by FT-IR spectroscopy a monomeric vanadyl and polymeric vanadates, the vanadyl/vanadate ratio remains practically constant.

Documentos Relacionados

• Síntese e caracterização textural do catalisador CeO2/TiO2 obtido via sol-gel: fotocatálise do composto modelo hidrogenoftalato de potássio
• Híbridos à base de anilina/sílica obtidos através do processo sol-gel: síntese, caracterização e propriedades
• Sol-Gel TiO2 thin films sensitized with the mulberry pigment cyanidin
• "Incorporação de Er em SnO2 obtido via sol-gel: uma análise de xerogéis e filmes finos"
• Estudo de filmes finos e materiais particulados de TiO2 e de Ag/TiO2 produzidos pelo processo sol-gel