Caracterização de cerâmicas porosas de alumina reforçada com zircônia produzidas pelo método da réplica

AUTOR(ES)

Fernando Barcelos Marcolino de Souza

DATA DE PUBLICAÇÃO

2008

RESUMO

Porous ceramics have many applications: thermal insulation, catalytic support, materials to fire protection, filters, and others. There are many techniques to production of ceramic filters. One technique to obtain ceramic filters is the replication method. This method consists in the impregnation of polymeric foam with ceramic slurry followed by a heating treatment that will burn out the organic elements and sintering of the material, resulting of a replication of the original foam. To perform their functions ceramic filters must satisfy mechanical requirements and permeability parameters (darcian k1 and no-darcian k2). The permeability and the strength of the ceramic material are dependent of the pore size and pore distribution. To the use at high temperatures the evaluation of mechanical properties in these temperatures is necessary. In this work the mechanical behavior of two commercial porous ceramics (10 and 40 poros per inch) was studied these materials were submitted to compression and four-point flexure test (room temperature, at 1000 C, after thermal shock). Density and porosity measurements, permeability tests and microstructural analysis by scanning electronic microscopy (SEM) were realized. The Results showed that the decrease of mechanical strength of these materials, when submitted to thermal shock, occur for propagation of new cracks from cracks pre-existing and the permeability depends of the pore size

ASSUNTO(S)

método da réplica cerâmicas porosas replication method engenharia mecanica porous ceramics comportamento mecânico mechanical behavior ceramic filters permeability filtros cerâmicos permeabilidade

Documentos Relacionados

• Obtenção de espumas cerâmicas a partir de resíduo da terra diatomácea e ignimbrita pelo método de réplica
• Caracterização de flogopita para processamento de filtros cerâmicos porosos pelo método da réplica
• A comparative study between alumina-tetragonal zirconia composites and alumina - niobia ceramics for structural applications
• Estudo comparativo de compósitos alumina-zircônia tetragonal e de cerâmicas de alumina aditivada com nióbia para aplicações estruturais
• Caracterização microestrutural de compósitos de hidroxiapatita-alumina confeccionados pelo método da esponja polimérica