Avaliação do desempenho do aço D6 tratado termicamente e netretado em plasma com gaiola catódica visando aplicação industrial
AUTOR(ES)
Maria Luisa Martins Mendes
DATA DE PUBLICAÇÃO
2008
RESUMO
In this research there was an evaluation of the best conditions of nitriding in plasma within a cathodic cage at an atmosphere of 80% N2-20%H2 in samples of tool manganese steel AISI D6, cold working, treated thermally in the following conditions: tension relief, treated thermally to temperature of maximum heat, temperate heat and temperate and temperate heat. A pressure of 2.5mbar and temperatures of 400 and 300C com treatment time of two and three hours were used to evaluate its performance as cutting tool (punch) of bicycle backs. Hardness, micro-structural aspects (layer thickness, interface, grain size etc), and crystal phases on the surface were appraised. When treated to tension relief, thermally treated to maximum heat temperature, temperature and temperate heat, the samples presented hardness levels of 243HV, 231HV, 832HV, and 653HV, respectively. The best nitrification conditions were: four hours and 300C for heat samples. A superficial hardness of 1000HV and a 108m thickness for the nitrided layer were found in these samples
ASSUNTO(S)
gaiola catódica aço aisi d6 nitretação a plasma cathodic cage plasma nitriding steel aisi d6 engenharia de materiais e metalurgica
Documentos Relacionados
- Avaliação do desempenho do aço AISI D2 tratado termicamente e nitretado em plasma com gaiola catódica visando aplicação industrial
- Nitretação em plasma com gaiola catódica: caracterização e avaliação do desempenho da camada nitretada em facas de corte
- Nitretação iônica em gaiola catódica do aço ferramenta tipo AISI D2 para trabalho a frio
- Nitretação iônica em gaiola catódica do aço inoxidável martensítico AISI 420
- Nitretação em plasma com gaiola catódica: investigação do mecanismo e estudo comparativo com a nitretação em plasma de tensão contínua