Analysis of the growth pattern of Vero cells cultured on dense and porous poly (L-Lactic Acid) scaffolds

AUTOR(ES)

Santos Jr, Arnaldo Rodrigues, Barbanti, Samuel Hilsdorf, Duek, Eliana Aparecida de Rezende, Wada, Maria Lucia Furlan

FONTE

Materials Research

DATA DE PUBLICAÇÃO

2009-09

RESUMO

Poly (L-lactic acid) (PLLA) polymers are the most frequently used substrates for cell culture, tissue regeneration and orthopedic prostheses, mainly because of their atoxic characteristics and good biocompatibility. The objective of this study was to evaluate whether a higher density or different pore diameters (less than 45, 180-250, and 250-350 µm) would change the growth pattern of cultured cells. The cells were found to adhere to and spread over all PLLA scaffolds studied. The cells also showed similar proliferation on dense and porous PLLA scaffolds, except for PLLA scaffolds with a smaller pore diameter. The cytochemical data showed high metabolic cellular activity on the various substrates. Overall, the results indicated satisfactory cell growth and proliferation on the different PLLA scaffolds studied, especially for those with pore diameters of 180-250 µm and 250-350 µm.

Documentos Relacionados

• Preparation and characterization of poly (L-lactic acid) and poly(ethylene oxide) blends
• CELL growth and viability analysis in poli membranes (L-lactic acid-CO-glycolic acid): an in vitro study
• Eletrofiação de nanocompósito de poli(L-ácido lático) com hidroxiapatita para regeneração óssea
• Use of poly (L-lactic acid) membranes in guided tissue regenation for periodontology
• In vitro degradation of Poly-L-co-D, L-lactic acid membranes